| Thickness | Assumed Density | Core Loss(W/Kg) | Core Loss(W/Lb) | Induction (800A/m) | Lamination Factor (Minimum) | Remark | ||
|---|---|---|---|---|---|---|---|---|
| mm | Kg/dm3 | 1.7T/50Hz | 1.7T/60Hz | 1.7T/50Hz | 1.7T/60Hz | |||
| 0.23 | 7.65 | 1.00 | 1.32 | 0.45 | 0.60 | 1.88 T | 94.5% | ¡@ |
| Assumed Density | Resistivity | Core Loss | Induction T | ||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| W¡þKg | W¡þLB | ||||||||||
| Kg/dm3 | Ohm*Meter (X10e-8) | 50Hz | 60Hz | 50Hz | 60Hz | ||||||
| 1.5T | 1.7T | 1.5T | 1.7T | 1.5T | 1.7T | 1.5T | 1.7T | 800A/m | 2,500A/m | ||
| 7.65 | 50 | 0.66 | 0.93 | 0.85 | 1.20 | 0.30 | 0.42 | 0.39 | 0.54 | 1.90 | 1.94 |
| Tensiile Strength | Yield Point | Elongation % | Hardness Hv(1) | Bending Test Value | Lamination Factor % | ||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| ¡@N/mm2¡@ | lb/in2(X10e3) | ¡@N/mm2¡@ | lb/in2(X10e3) | ||||||||||
| L | C | L | C | L | C | L | C | L | C | L | C | ||
| 363 | 412 | 53 | 60 | 353 | 363 | 51 | 53 | 5 | 30 | 188 | 14 | 9 | 97.7 |